合成氨中置锅炉的修复

本文在分析中置锅炉失效原因的基础上，提出了详细的修复措施，为类似情况的设备修复提供了借鉴。     

The corrosion behavior of sputter-deposited aluminum-tungsten alloys

Thin films on aluminum-tungsten alloys were prepared by co-deposition of pure aluminum and pure tungsten, each sputtered by an independently controlled magnetron source, on glass and sapphire substrates. Completely amorphous films were obtained in the Al₈₀W₂₀-Al₆₇W₃₃ composition range. Passivity and corrosion behavior of amorphous Al-W alloys were investigated in 1 M deaerated hydrochloric acid solution using polarization and impedance spectroscopy measurements and have been correlated with the properties of pure alloy components. Tungsten and sputter-deposited Al-W thin films are inherently passive materials while aluminum undergoes pitting corrosion in hydrochloric acid solution. The passive film formed at the OCP on each alloy possesses excellent electric and dielectric properties comparable to those of the isolating film on tungsten. The absolute impedance increases with increasing tungsten content in the alloy. According to electrochemical polarization measurements, alloying Al with W in solid solution significantly enhances the material's resistance to pitting corrosion by shifting the breakdown potential above 2000 mV (Al₆₇W₃₃) and lowering the corrosion rate at the OCP by more than two orders of magnitude. The most likely mechanism explaining the passivity of amorphous Al-W alloys, the Solute Vacancy Interaction Model (SVIM), involves the formation of complexes between highly oxidized solute atoms (W⁺⁶) and mobile cation vacancies, which restrict the transport of Cl⁻ through the oxide film and inhibit its breakdown in hydrochloric acid solution. The role that film stress relaxation effects and microscopic defects in amorphous Al-W films, of the some composition, and deposited on various substrates play in their corrosion resistance is discussed.     

φ1m氨合成塔20钢异径管失效分析

分析了氨合成塔底部副线20钢异径管爆破的原因。结果表明：异径管长期处于200℃以上工作，管内H2与管材中的碳或Fe3发生化学反应，生成CH4致使管内脱碳并产生裂纹，异径管强度降低脆性增加，导致爆破。     

换热站容积式加热器管束失效原因及防护

对换热站容积式加热器管束失效原因进行了分析 ,指出主要是由于汽蚀和电化学腐蚀所致。从操作工艺和采用 12Cr2AlMoV材质两方面进行改进 ,可使管束的使用寿命由 4个月延长到 2年     

Inhibition of atmospheric corrosion of mild steel by sodium benzoate treatment

The objective of this study was to evaluate the effectiveness of sodium benzoate as an inhibitor to slow down or prevent atmospheric corrosion/discoloration of the local mild steel during storage in the Arabian Gulf region. Test specimens were prepared from locally produced reinforcing steel products. The inhibitor solution was applied on steel specimens at a concentration of 100 mM for 1 day at room temperature. Wooden exposure racks were used to hold as-received and inhibitor-treated specimens during atmospheric exposure for different periods. Corrosion was evaluated through weight loss determination and electrochemical technique. As expected, the Arabian Gulf atmosphere was corrosive on the as-received local mild steel. On the other hand, treatment of steel with sodium benzoate lowered its corrosion rate during initial days of its exposure to atmosphere. However, atmospheric corrosion inhibition performance of sodium benzoate deteriorated with exposure time after 30 or more days of atmospheric exposure, and the corrosion rates of sodium benzoate-treated specimens reached that of the unprotected specimens at the end of 90 days of atmospheric exposure.     

浅析6063铝型材表面“铝丝印”的成因与对策

在介绍“铝丝印”概念的基础上，从金属腐蚀学的观点出发，分析了“铝丝印”形成的电化学腐蚀机理，并提出了具体的解决措施。     

长距离油、气、水混输管道内壁流动腐蚀的研究进展

就近几十年来，多相流管线的流动腐蚀（CO2腐蚀，H2S腐蚀，腐蚀/冲蚀协同作用），腐蚀/冲蚀数学模型和设计准则，腐蚀检测，腐蚀防护与控制技术等方面的研究进展进行了综述。指出了当前研究中所存在的一些问题，就多相流的研究方向提出了相应的建议。     

高温预析出对Al-Zn-Mg系铝合金时效硬化和应力腐蚀的影响

研究了高温固溶后降温处理工艺对中强可使预析出LC52和7039铝合金的组织、时效硬化和应力腐蚀的影响。金相观察发现,高温预析出可优先在晶界处产生,并提高随后时效状态下晶界析出相的不连续分布程度,温度降低到一定程度晶内和晶界产生大量析出。合金拉伸性能和应力腐蚀结果表明,预析出在保持强度和塑性的同时,可提高抗应力腐蚀性能。而预析出温度降低,合金强度呈下降趋势。     

输油管线防垢防腐及新药剂试验

讨论影响输油管线结垢和腐蚀的主要因素，从理论上分析了结垢形成，推导计算结垢量的公式。介绍了输油管线防止硫酸钡垢的清防方法。     

EIS evaluation of the filiform corrosion of aluminium coated by a cataphoretic paint

Filiform corrosion is mainly considered as a cosmetic attack and is undesirable in most applications. The initiation and propagation of the filaments are related to different parameters such as the presence of defects, the permeability of the coating to water and oxygen, the adherence of the paint system and the presence of salts.

The aim of this work is to study the behaviour of painted aluminium samples towards filiform corrosion or delamination. The 6082 Aluminium alloy was selected and the samples were covered with a cataphoretic epoxy primer without lead (PPG Industries France). Prior to the application of the electrocoat, the samples were pre-treated by a commercial Zr/Ti or chromate conversion treatment or simply etched with a commercial acid etching product.

Filiform corrosion was studied by the normalized test (ISO/DIS 4623): painted and scratched samples were inoculated in HCl and exposed in a constant humidity chamber at 40 °C and 82% RH for 3 weeks. After exposure the samples were subjected to a visual and optical microscopic examination.

Electrochemical impedance spectroscopy was used to study the sensitivity to filiform corrosion. The operating mode of this test is similar to the normalized one. The samples were scratched before inoculation for 1 h in HCl and then exposed to the humidity chamber for a maximum of 4 days. The samples were tested by EIS in an acidified 0.1 M Na₂SO₄ electrolyte solution. The resulting impedance spectra were analyzed with an appropriate equivalent electrical circuit which allows the evaluation of the exposed metallic surface area, directly related to the extent of filiform corrosion or delamination. Different parameters were varied: the exposure time in the humidity chamber; the immersion time in the electrolyte sulphate solution as well as its pH and the coating thickness.